Additive Manufacturing (AM) processes are known as revolutionary manufacturing processes that fabricate a part using a 3D model layer upon layer. These techniques gained more attention from various industries due to their advantages like low waste material. Also, these processes can produce any part with high degrees of complexity in a short period of time. The Fused Deposition Modeling (FDM) process is a material extrusion-based technique which works by extruding a fine molten polymeric filament through a heated nozzle on the heated platform named printer bed. In this method, some important manufacturing parameters play a crucial role in controlling the mechanical properties and quality of the final fabricated part. However, all printed specimens through the FDM process should be tested based on the standards under some critical circumstances. Thus, in the current research paper, five and three test speeds are considered in tensile and fracture testing procedures, respectively to evaluate how these speeds can affect the mechanical and mode I fracture properties. Also, as the FDM specimens present elastic-plastic behavior, the critical value of J-integral is assumed as a fracture assessment and calculated from the finite element analysis. Among the mechanical properties, ultimate tensile strength is affected significantly by the test speed. For instance, the ultimate tensile strength of FDM specimens is 39.02, 38.58, 42.33, 48.09, and 52.11 for test speeds of 2, 4, 6, 8, and 10 mm/min, respectively. But vice-versa results are detected for the mode I fracture behavior and corresponding values of J for the FDM-PLA specimens. Finally, experimental and numerical results together with comprehensive discussions about the considered speeds and obtained results are reported.
© 2024. The Author(s).